Product Details:
Payment & Shipping Terms:
|
| Appearance: | Colorless Transparent Pellets | Package: | 25kg Bag |
|---|---|---|---|
| Composition: | Phenolic Novolac Resin | Curing Temperature: | 150-180°C |
| Features1: | High Purity For Electronic Grade | Features2: | Improved Heat Resistance |
| Features3: | Low Viscosity | ||
| High Light: | phenalkamine epoxy hardener,cycloaliphatic amine hardener |
||
Phenolic Novolac resin is produced by condensing phenol with an insufficient amount of formaldehyde to complete the reaction in the presence of an acid catalyst. This produces a thermoplastic resin.
Phenolic Novolac resins are also used as curing agents or hardeners for epoxy resins in applications such as molding materials, laminates, coatings and adhesives. The phenolic novolac resins used are non-heat reactive materials by themselves, but have phenolic-OH groups that react with epoxy groups. Since the curing mechanism does not produce by-products, thick sections may be obtained without voids and stresses and with low shrinkage.
Application
Adhesives & sealants, Epoxy hardeners and additives, High-temperature applications, Protective coatings
Specification:
| Properties | Value |
| Curing time @150°C | 100-160s |
| Flow Distance@125°C | min120mm |
| Free-phenol | max.0.1% |
| Cone & plate viscosity | 0.3P |
| Conductivity,μS/cm | max.3 |
| Sodium content, AA | max.5ppm |
| Chloridion,AA | max.5ppm |
| Hydroxyl equivalent weight,g/eq | 103-109 |
| Softening point,°C | 67-72 |
| Karl Fischer water content | max.0.5% |
Packing&Storage
the package is paper-plastics bag in 25KGS each one
The storage life of this product is several months in a cool and dry place in original closed bags